Moisture — where it appears

The water content of a material, which changes its strength, its stiffness and its dimensions. Timber's duration-of-load effect is stronger when it is wet, and its shrinkage and swelling with humidity are movements of the same order as a thermal one.

Named by 2 essays across one field — each of them below, with the objects they name alongside it.

Strength at an angle, and the straight line that is not it. Compressive strength against the angle between the load and the grain. Hankinson's formula — f₀f₉₀ ÷ (f₀sin²α + f₉₀cos²α) — is an interpolation rather than a failure theory, and what makes it worth having is how far it sits from the straight line anyone would otherwise draw between 21 and 2.5 N/mm². At forty-five degrees it gives 4.5 N/mm² against the line's 11.8: 38 per cent of it, and 21 per cent of the strength along the grain. The curve drops away in the first twenty degrees because the weak direction starts governing as soon as it has any component at all, which is the same arithmetic as a section's weak axis and the reason a skewed bearing detail is a real loss rather than a small one.

The material that has a direction

Every material in this collection so far has had one modulus and one strength. Timber has three of each, differing by more than an order of magnitude, and the consequence is not a correction to steel design — it is a different set of checks with a different one governing.

materials · anisotropy Ten decades of time for forty per cent of the strength. Strength as a fraction of the five-minute test value, against the length of time the load is held, over 12 decades of seconds. The relation is a straight line on this axis, which is the reason a single duration factor works at all: every decade of time costs about the same amount of strength. A load held for 60 years leaves 59% of the short-term strength, and the member need not have moved — this is not creep, and it is not fatigue, because nothing about the load varies. It is that a static stress slowly breaks fibres. The curve has an asymptote at 18% that nobody quotes: below about a fifth of its short-term strength a member has no time to failure at all, so there is a stress under which duration stops being a question rather than merely becoming a small one.

The load that was left on too long

A timber beam that carries a load for fifty years fails at about fifty-nine per cent of the stress the same beam carries for five minutes in a testing machine. Nothing about the load varies, the member need not have deflected, and the relation between the two is a straight line on a logarithmic time axis over ten decades.

materials · duration of load

Named alongside it

The objects these essays reach for when they reach for this one.

AnisotropyTimberBearingCharacteristic strengthCreepCreep ruptureDamage accumulationDuration of loadElastic modulusFatigueFractureGrain