The change in concrete's properties with its age at loading, as hydration goes on for months after casting. A member loaded young creeps more than the same member loaded old, which is why the age at first load enters a creep coefficient, and why strength and stiffness do not develop together.

Named by 5 essays across one field — each of them below, with the objects they name alongside it.

The stress that leaks away. A restrained shrinkage strain of 320 microstrain in concrete of modulus 34000 N/mm². Ignoring creep it produces 10.88 N/mm², which is above the tensile strength of 3.8 and predicts that every restrained concrete member ever cast has cracked. Counting creep by the superposition integral leaves 1.72 N/mm² after 55 years, and the one-line age-adjusted shortcut at the usually quoted ageing coefficient of 0.8 leaves 3.05. The two disagree — this creep function implies an ageing coefficient of 1.67, not 0.8 — and both are below the tensile strength, so the conclusion turns on counting creep at all rather than on how it is counted.

The stress that leaks away

Creep makes a load's deflection grow and an imposed strain's stress shrink, and the second is why restrained concrete does not crack as often as an elastic calculation says. The same material property runs both ways, and which way it runs depends on whether the structure was given a force or a movement.

materials · Creep Half of the creep is the member drying out. The creep coefficient of a concrete of mean strength 38 N/mm² loaded at 28 days, in a member of notional size 150 mm, against time since loading: exposed to air at 50 per cent relative humidity, and the same member sealed so that it cannot dry. After a year the exposed member's coefficient is 1.93 and the sealed member's 0.81; after 50 years they are 2.45 and 1.28. The shaded difference, 48 per cent of the exposed member's final creep, is what drying adds. The sealed member's coefficient has no size in it; the drying part is where the member comes in.

The creep that belongs to the member

A creep coefficient is quoted for a concrete, and half of it is not a property of the concrete. It is the member drying out, and drying goes through the surface — so one mix creeps a quarter more in a thin slab than in a deep beam, gets there years sooner, and in saturated air forgets its size altogether.

materials · Creep The humidity through a slab's depth, and the strain it asks for. A slab 200 mm thick drying through its top face only into air at 50 per cent, with its underside sealed by a steel deck. Left, the pore humidity against depth at 28 days — 50 per cent at the surface and 100 at the base; 90 days — 50 per cent at the surface and 100 at the base; 1 year — 50 per cent at the surface and 99 at the base; 5 years — 50 per cent at the surface and 74 at the base; 20 years — 50 per cent at the surface and 51 at the base. Right, the free strain each of those profiles asks for, taken as shrinkage at the local humidity. At 28 days the top wants to be 461 microstrain shorter than it was and the bottom 0; at 20 years the two are 461 and 456, and the gradient that produced the curl has gone. Not one of the profiles is straight, and a section that stays plane cannot deliver any of them.

The slab that dries from one face

A creep coefficient is one number for a member, and a member drying through one face does not have one. Give every depth its own humidity and the section a strain profile it cannot deliver, and two things follow that no single coefficient contains — a six-metre slab lifts eleven millimetres at its edges with nothing on it, and its top surface is past cracking before it has been loaded.

materials · Creep Three moment diagrams for one pair of beams. Two 15 m spans carrying 12.0 kN/m, drawn sagging downward. As built they are simple spans: 337.5 kN·m at each midspan and nothing over the middle support. Built monolithic they would carry 337.5 kN·m of hogging over the support and 168.8 at midspan. Loaded at 28 days and made continuous at 60, creep takes them 46 per cent of the way from the first to the second: 155.2 kN·m over the support and 259.9 at midspan, after twenty years in which nothing about the loading changed. The support had no moment on the day it was cast and no drawing of the finished structure shows why it has one now.

The support that had no moment when it was cast

Two beams are set on their bearings, carry their own weight for a month, and are then stitched together over the middle support. Nothing about the loading changes afterwards. Twenty years later the stitch is carrying 155 kilonewton-metres, because the concrete went on creeping and the joint would not let it — and how much arrives is decided by a crane schedule.

materials · Creep Where a tendon's force goes, over fifty years. The loss of stress in a tendon stressed to 1300 N/mm² and released at 7 days into a member of notional size 300 mm at 70 per cent humidity, with the three causes stacked. At 28 days the total is 61.9 N/mm²; at a year 131.5; at fifty years 190.8, which is 14.7 per cent of what the tendon started with. Creep supplies 107.7 of that, drying and autogenous shrinkage 50.6, and the steel's own relaxation 32.5. Half the loss has happened by 119 d and nine-tenths by 8 y.

The prestress the member takes back

A tendon is stretched, locked off against the concrete, and then has to hold that extension while the concrete underneath it shortens by itself. Fifteen per cent of the force goes, most of it to creep, and how much goes is decided by the shape of the member and the air it stands in rather than by anything about the steel.

materials · Creep

Named alongside it

The objects these essays reach for when they reach for this one.

CreepImposed deformationServiceabilityEffective modulusShrinkageModulusRelaxationSuperpositionBuild sequenceCurvatureDeflectionForce method