Heat-affected zone — where it appears

The strip of parent metal beside a weld whose properties the welding heat has changed. In a heat-treated or work-hardened aluminium alloy it loses up to half its proof stress, so it decides both the member's strength and where the member stretches before it fails.

Named by 2 essays across one field — each of them below, with the objects they name alongside it.

The strength was bought in a furnace and the welder gives it back. Proof stress as delivered and beside a weld, for four aluminium alloys. The heat-treated alloys lose half of it: the strength of a 6xxx extrusion is in precipitates formed by an ageing treatment, and the arc dissolves them for 32 mm either side of the weld, permanently. The work-hardened tempers lose nearly as much, because the heat undoes exactly the work. The annealed ones lose nothing at all, because there is nothing left in them to anneal. The consequence is the crossover: 5083-H22 is 1.04 times 6061-T6 as delivered and 0.92 times it once welded, so the stronger alloy is the weaker member. The 240 mm member drawn, with two longitudinal welds, keeps 87% of its parent capacity — a weld along a member softens a strip and leaves a section, and the same weld across it softens the whole of one.

The strength the welder gives back

A 6082-T6 extrusion is twice as strong as a 5083-H111 plate and, welded across, the two are within a few per cent of each other. The heat of the arc anneals the metal for thirty millimetres either side, permanently, and the strength that was bought in a furnace is given back at the first joint.

materials · Heat-affected zone Ductile until it was welded. A 2.0 m 6082-T6 member pulled in tension, as supplied and with one weld across it whose heat-affected zone is 60 mm long: the load per unit of parent section against the member's overall strain, to the maximum load, where the weaker part begins to neck. The plain member reaches 310 N/mm² at 7.0% strain, 140 mm of stretch. The welded one reaches 185 N/mm² at 0.62%, 12.3 mm — 8.8% of the plain member's, and the parent never reaches its proof stress of 260 N/mm². (uniform elongations assumed: 7.0% for the parent, 12% for the zone)

The soft zone that takes all the stretch

The metal beside a weld in heat-treated aluminium is weaker than the rest of the member and more ductile, and it is tempting to read the second fact as a consolation. It is not. A member welded across stretches only where it is weak, and the weak zone is sixty millimetres long; a two-metre 6082-T6 tie that would extend 140 mm before necking extends 12 mm once welded, and the parent metal never yields at all. What decides it is one ratio, the zone's ultimate strength over the parent's, and the ductility returns only when that ratio reaches one.

materials · Heat-affected zone

Named alongside it

The objects these essays reach for when they reach for this one.

AluminiumDuctilityNet sectionProof stressWeldAnnealingEffective sectionFabricationFatigueLocalisationMaterial selectionNecking