Damage — where it appears

The fraction of a detail's fatigue life used up by a set of cycles, summed over a spectrum as n/N band by band. It is a bookkeeping quantity rather than a measurable state: it carries no information about the crack, which is why a rule built on it cannot see the order the cycles arrived in.

Named by 2 essays across one field — each of them below, with the objects they name alongside it.

Two per cent of the traffic and most of the damage. A 120-year traffic spectrum on one detail of category 71, with each band's share of the cycles and its share of the damage. The two bars have almost nothing to do with one another, and the reason is the slope of three: life goes as the inverse cube of the stress range, so a cycle twice as large does eight times the damage and a cycle a third as large does a twenty-seventh of it. A full train is 2% of the crossings and 58% of the damage; and three of the five bands — an ordinary lorry, a van, a car, 90% of the crossings — sit under the cut-off and do none of it at all. The equivalent constant range that would do the same damage in the same number of cycles is 25.5 N/mm², which is the one number a designer is usually handed — and it is a cube-weighted average, so it is nearer the heaviest vehicle than to the average one.

The cycles that do not count

A fatigue spectrum has to be reduced to one number, and the reduction is a cube-weighted average rather than an ordinary one. Two per cent of the traffic does most of the damage, ninety per cent of it does none at all, and the equivalent range that comes out is nearer the heaviest vehicle than the average one.

materials · Fatigue The same cycles, and two different lives. Two sequences made of exactly the same cycles — blocks of 6.00M at 40 N/mm² alternating with blocks of 0.22M at 90, on a detail starting with a 0.50 mm flaw. Taking the small cycles first, the crack reaches its critical 87.7 mm after 12.36M cycles; taking the large ones first, after 6.36M. Miner's sum at the moment of failure is 0.99 for the first and 0.68 for the second, so a rule that predicts failure at a sum of one is right to within a per cent about the first and 48 per cent unconservative about the second. The mechanism is on the axes: ΔK rises with the crack, so a large block met late finds a longer crack and does more with it.

The record played backwards

Miner's rule adds damage, and a sum has no order. A crack does, twice over: a large block met late finds a longer crack and does more with it, and an overload leaves a plastic zone that slows everything after it. The same cycles rearranged fail at 12.4 million or at 6.4, and a Miner sum that is right to one per cent about the first is out by half about the second. One cycle in four million can add fifty-four per cent to a life.

materials · Fatigue

Named alongside it

The objects these essays reach for when they reach for this one.

FatigueMiners ruleSpectrumCrack growthCut-off limitCycle countingDetail categoryEndurance limitEquivalent rangeFree bodyInspectionPlastic zone