Triaxiality — where it appears

The ratio of hydrostatic to deviatoric stress at a point, which decides how much a material can deform before it fractures. Yielding does not care about the hydrostatic part and fracture does, so a neck or a notch that raises triaxiality embrittles a material that is ductile in simple tension.

Named by 2 essays across one field — each of them below, with the objects they name alongside it.

The same steel, brittle in January. Fracture toughness against temperature for a 25 mm ferritic plate, from Wallin's master curve — 30 + 70·exp(0.019(T − T₀)) in MPa√m, whose shape is the same for every ferritic steel and whose only free parameter is the reference temperature T₀ = -60 °C. Beside it, and on its own scale, is the crack length that toughness will tolerate at 200 N/mm², which goes as the square of it. At +20 °C this plate carries a 764 mm flaw and at -20 °C it carries 199 mm — a factor of 3.8 for a forty-degree change in the weather, in a steel that met its specification on both days. Thickness moves the curve as well, and the wrong way: constraint at a crack tip suppresses the yielding that would have blunted it, so a 100 mm plate of this steel tolerates 27% of the flaw a 10 mm plate does. Loading it in a millisecond shifts the whole curve another forty degrees.

The same steel, brittle in January

Every other material property in this collection is a number. Toughness is a curve, and the axis it runs along is temperature. Between twenty degrees and minus twenty a structural steel does not get gradually weaker — it changes the mechanism by which it fails, and the flaw it will tolerate falls by a factor of four.

materials · Transition temperature The curve the machine drew and the curve the material was on. The same tensile test twice. Force over the ORIGINAL area against extension over the original length is the engineering curve, which peaks at 431 MPa and 24.6 per cent and then falls. Force over the ACTUAL area against the natural logarithm of the length ratio is the true curve, which passes 538 MPa at the same instant and keeps rising. Nothing softens anywhere on this figure: the descending branch is the original area still being divided by, and the material is hardening the whole way. The two separate at the very first plastic strain and the gap between them is exactly e^ε, which is 1.25 at the ultimate load. Past that instant the deformation stops being uniform, so the engineering curve is drawn dashed: the real one falls faster than this, because the extension is now happening in one short length of the bar and the strain axis is still dividing it by the whole gauge.

The curve was rising the whole time

Every tensile curve ever printed turns over and falls, and nothing about the material does. The fall is the original area still being divided by after the specimen has stopped having it — and correcting the two denominators turns a strength, a ductility and a failure into one exponent.

materials · Gauge length

Named alongside it

The objects these essays reach for when they reach for this one.

DuctilityBrittle failureCharpyConstraintCrack growthFatigueFlawGauge lengthLocalisationMaster curveNeckingPlastic strain