Weakest link — where it appears

The model of a strength that belongs to the worst flaw in a volume or along a length, so that more material means a lower expected strength. It gives the Weibull distribution, and it is why a longer crack front or a larger member fails at a lower stress than the specimen.

Named by 2 essays across one field — each of them below, with the objects they name alongside it.

The characteristic strength, which nothing was measured at. A lognormal population of strengths with a mean of 30 N/mm² and a coefficient of variation of 0.15. The characteristic value is the 5% fractile — 23.2 N/mm², which is 77% of the mean, and which need not be the strength of any specimen that was tested. Dividing it by 1.50 gives 15.5, and the shaded sliver below that is the fraction of the population that would fail to reach it: 6.4e-6, or one in 155,818. A factor applied to a fractile is not covering the scatter, because the scatter has already been spent getting to the fractile.

The strength no specimen had

A material property is written into a calculation as a number, and a material does not have one. It has a population of strengths with a mean and a spread, and the number used is a low fractile of that population — a value that need not have been measured, that most of the material exceeds, and whose distance below the mean is decided entirely by the scatter.

materials · Characteristic strength One steel, one crack, three plates. The strip-yield failure stress of plates with an edge crack, at −20 °C in a grade 355 steel whose master-curve reference temperature is −38 °C, against the crack length on a logarithmic scale, for plates 12, 25 and 60 mm thick, each with the toughness of its own crack front at the 5 per cent level: 88, 77 and 66 MPa√m. At a 20 mm crack the 12 mm plate fails at 267 N/mm², the 25 mm plate at 242 and the 60 mm plate at 214. Dashed, the simple check with the 25 mm toughness, the lower of fracture and yield: 274 N/mm² at the same crack, for every thickness.

The toughness that belongs to the plate

A steel's cleavage toughness is measured on a specimen 25 mm thick, and a crack through a plate starts at the weakest spot its front passes through — so a crack through a 60 mm flange samples more weak spots than the test did, and is less tough, and one through a 12 mm web samples fewer. Put each plate's own toughness into the strip-yield assessment and the simple check, which overstates a cracked plate by 23 per cent at the specimen's thickness, overstates a 60 mm flange by 36 per cent and a 100 mm plate by 45, while a thin web pays much of the strip-yield debt back.

materials · Fracture

Named alongside it

The objects these essays reach for when they reach for this one.

FractureSize effectBrittle fractureCharacteristic strengthCoefficient of variationCritical crackDuctilityFractileFracture toughnessLognormalMaster curvePartial factor