Fracture — the series

One essay so far on this idea, and more questions about it than one essay answers.

$The crack length at which the strength stops mattering. Failure stress against crack length for a toughness of 100 MPa√m, with two steel grades drawn. The falling curve is fracture — Kc divided by Y times the root of pi a — and it does not know what the yield stress is. The horizontal lines are the grades. At 275 N/mm² the two cross at a crack 33.5 mm long; At 460 N/mm² the two cross at a crack 12.0 mm long. The stronger grade's transition is the shorter one — raising the yield stress does not raise the strength of a cracked member, it only shortens the crack that takes it away.$
The flaw that sets the strength

A member with a crack twenty millimetres long fails at its yield stress. Make the steel stronger and the crack that does it gets shorter, so the same flaw that was harmless in the weaker grade decides the stronger one.
part 1 · materials