The load-duration generator

Rendered here at the parameters it defaults to, with every essay that calls it — which is the same list as the blast radius of changing it.

Ten decades of time for forty per cent of the strength. Strength as a fraction of the five-minute test value, against the length of time the load is held, over 11 decades of seconds. The relation is a straight line on this axis, which is the reason a single duration factor works at all: every decade of time costs about the same amount of strength. A load held for 50 years leaves 59% of the short-term strength, and the member need not have moved — this is not creep, and it is not fatigue, because nothing about the load varies. It is that a static stress slowly breaks fibres. The curve has an asymptote at 18% that nobody quotes: below about a fifth of its short-term strength a member has no time to failure at all, so there is a stress under which duration stops being a question rather than merely becoming a small one.

1 essay calls load-duration. The drawing above is what it returns with no arguments at all; every call below passes it something, because a placement that passes nothing draws whichever member of the family the generator happens to default to rather than the one its essay argues about.

Where it is called

Changing this generator changes every one of these figures.

$Ten decades of time for forty per cent of the strength. Strength as a fraction of the five-minute test value, against the length of time the load is held, over 12 decades of seconds. The relation is a straight line on this axis, which is the reason a single duration factor works at all: every decade of time costs about the same amount of strength. A load held for 60 years leaves 59% of the short-term strength, and the member need not have moved — this is not creep, and it is not fatigue, because nothing about the load varies. It is that a static stress slowly breaks fibres. The curve has an asymptote at 18% that nobody quotes: below about a fifth of its short-term strength a member has no time to failure at all, so there is a stress under which duration stops being a question rather than merely becoming a small one.$ Materials

The load that was left on too long

A timber beam that carries a load for fifty years fails at about fifty-nine per cent of the stress the same beam carries for five minutes in a testing machine. Nothing about the load varies, the member need not have deflected, and the relation between the two is a straight line on a logarithmic time axis over ten decades.